Shoes With Resin
Huada Chemical Group as the domestic PU resin for shoe soles professional production enterprises. Always adhere to provide customers with stable quality, quality products and constantly enrich their product lines. Customized development services can be provided according to the personalized needs of customers.
1
High Hardness Polyester
| HT-5890T/F-2280 |
| 1、特性：高硬度，中低密度 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：立跟鞋底，高坡跟 | |||||||||||||||||
| Application：Sole for casual shoes and man shoes | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5890T | 液狀或石蠟狀 | 600~1000 | 1.160~1.180 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2280 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5890T | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2280 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/116~118 | 7~10 | 40~60 | 0.24~0.27 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.50~0.65 | 80~90 | 50~58 | 320~400 | 32~37 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5885B/F-2260 |
| 1、特性：高硬度，中低密度 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：立跟鞋底，高坡跟 | |||||||||||||||||
| Application：Sole for casual shoes and man shoes | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5885B | 液狀或石蠟狀 | 600~1000 | 1.160~1.180 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2260 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5885B | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2260 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/135~137 | 6~9 | 30~38 | 0.20~0.23 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.40~0.45 | 85~92 | 50~63 | 320~400 | 30~35 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
2
Medium Hardness Polyester
| HT-5600/F-2180 |
| 特性：中高硬度，中高密度 | ||||||||||||||||
| Characteristic：Medium to high hardness and medium to high density | ||||||||||||||||
| 2、用途：皮鞋、涼鞋 | ||||||||||||||||
| Application：Sole for casual shoes and man shoes | ||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | ||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | ||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | ||||||||||||
| HT-5600 | 液狀或石蠟狀 | 500~900 | 1.160~1.180 | 18 | ||||||||||||
| liquid or waxy solid | ||||||||||||||||
| F-2180 | 液狀或石蠟狀 | 200~600 | 1.190~1.210 | 20 | ||||||||||||
| liquid or waxy solid | ||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | ||||||||||||||||
| 4、物料預熱 Materials preheat | ||||||||||||||||
| HT-5600 | 60-70℃預熱6~8h | |||||||||||||||
| Preheated at 60-70℃ for 6~8h | ||||||||||||||||
| F-2180 | 60-70℃預熱8~12h | |||||||||||||||
| Preheated at 60-70℃ for 8~12h | ||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | ||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/119~120 | 8~10 | 50~60 | 0.23~0.27 | 45~55 | ||||||||||
| Parameter | ||||||||||||||||
| ◎催化劑SM-2的加入量為230±5g/18kg The adding content of SM-2 should be 230±5g / 18kg | ||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | ||||||||||||||||
| 6、制品性能 Physical properties | ||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | ||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | ||||||||||
| 物性值 | 0.55~0.65 | 65~72 | 50~57 | 350~420 | 33~40 | 300000次無裂口 | ||||||||||
| Physical properties | 300000 times no crack | |||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | ||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | ||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | ||||||||||||||||
| Free rise density may vary with temperature &humidity. | ||||||||||||||||
| HT-5606/F-2180 |
| 1、特性：表面光亮，手感柔和 | |||||||||||||||||
| Characteristic：smooth surface and good handle | |||||||||||||||||
| 2、用途：皮鞋、涼鞋 | |||||||||||||||||
| Application：Sole for casual shoes and man shoes | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5606 | 液狀或石蠟狀 | 800~1200 | 1.120~1.200 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2180 | 液狀或石蠟狀 | 200~600 | 1.190~1.210 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5606 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2180 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/99~101 | 7~10 | 50~60 | 0.23~0.30 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為240±5g/18kg The adding content of SM-2 should be 240±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.55~0.65 | 58~65 | 50~57 | 370~450 | 33~40 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5608B/F-2180 |
| 1、特性：中等密度，成型性好 | |||||||||||||||||
| Characteristic： medium density and good moldability | |||||||||||||||||
| 2、用途：休閑鞋、涼鞋 | |||||||||||||||||
| Application：Sole for casual shoes and man shoes | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5608B | 液狀或石蠟狀 | 500~900 | 1.160~1.180 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2180 | 液狀或石蠟狀 | 200~600 | 1.190~1.210 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5608B | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2180 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/116~118 | 9~11 | 40~60 | 0.22~0.25 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為270±5g/18kg The adding content of SM-2 should be 270±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.46~0.55 | 60~65 | 48~55 | 350~450 | 32~37 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5650/F-2280 |
| 1、特性：成型性好，輕便 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：女鞋、休閑鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5650 | 液狀或石蠟狀 | 800~1200 | 1.160~1.180 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2280 | 液狀或石蠟狀 | 200~600 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5650 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2280 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/84.5~86.5 | 7~10 | 30~40 | 0.22~0.26 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 水H2O 35±5g/18kg | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.45~0.55 | 58~65 | 45~60 | 370~470 | 30~35 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5660/F-2280 |
| 1、特性：成型性好，輕便 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：沙灘鞋、休閑鞋 | |||||||||||||||||
| Application：Sole for casual shoes and man shoes | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5660 | 液狀或石蠟狀 | 1600~2000 | 1.150~1.170 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2280 | 液狀或石蠟狀 | 200~600 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5660 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2280 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/119~120 | 7~9 | 35~45 | 0.23~0.28 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 水H2O 35±5g/18kg | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.48~0.55 | 55~65 | 45~55 | 350~450 | 30~35 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-8807/F-2500 |
| 1、特性：表皮好，成型性好，手感好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：皮鞋、涼鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-8807 | 液狀或石蠟狀 | 800~1400 | 1.160~1.200 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2500 | 液狀或石蠟狀 | 200~600 | 1.190~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-8807 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2500 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/100~102 | 6~9 | 30~40 | 0.23~0.27 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.45~0.55 | 55~65 | 40~55 | 400~480 | 20~25 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
3
Soft Polyester
| HT-5830L/F-2580L |
| 1、特性：低硬度，手感好，耐寒性 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：連幫鞋和休閑鞋底 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5830L | 液狀或石蠟狀 | 800~1200 | 1.170~1.190 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2580L | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5830L | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2580L | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/54.5~56.5 | 7~10 | 40~60 | 0.21~0.25 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality 水H2O 50±5g/18kg | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -20℃ | |||||||||||
| 物性值 | 0.42~0.50 | 30~40 | 30~50 | 500~700 | 15~25 | 40000次無裂口 | |||||||||||
| Physical properties | 40000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5835/F-2280 |
| 1、特性：低硬度，手感好，耐水解 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：連幫鞋和休閑鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5835 | 液狀或石蠟狀 | 1000~1800 | 1.110~1.130 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2280 | 液狀或石蠟狀 | 200~600 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5835 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2280 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/62~64 | 7~10 | 40~60 | 0.21~0.25 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為350±5g/18kg The adding content of SM-2 should be 350±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.42~0.50 | 35~40 | 30~45 | 340~400 | 30~35 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5840/F-2290 |
| 1、特性：低硬度，手感好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：連幫鞋和休閑鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5840 | 液狀或石蠟狀 | 1000~1800 | 1.170~1.190 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2290 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5840 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2290 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/70~72 | 7~10 | 50~60 | 0.27~0.32 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at 23℃ | |||||||||||
| 物性值 | 0.55~0.65 | 35~40 | 25~45 | 340~400 | 30~35 | 300000次無裂口 | |||||||||||
| Physical properties | 300000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5640/F-2680 |
| 1、特性：低硬度，手感好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：連幫鞋和休閑鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5640 | 液狀或石蠟狀 | 800~1600 | 1.140~1.160 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2680 | 液狀或石蠟狀 | 200~600 | 1.170~1.190 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5640 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2680 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/81~83 | 6~10 | 35~50 | 0.22~0.30 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality 水H2O 50±5g/18kg | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -20℃ | |||||||||||
| 物性值 | 0.40~0.55 | 35~40 | 30~40 | 350~400 | 25~30 | 50000次無裂口 | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-6730/F-2180 |
| 1、特性：手感柔軟，成型性好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：鞋墊 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-6730 | 液狀或石蠟狀 | 800~1600 | 1.080~1.160 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2180 | 液狀或石蠟狀 | 200~500 | 1.190~1.210 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-6730 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2180 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/70~72 | 6~9 | 45~55 | 0.13~0.16 | 45~55 | 5~7 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑的加入量為260±5g/18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | ||||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore C） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | ||||||||||||
| 物性值 | 0.25~0.35 | 25~40 | 15~30 | 250~350 | 10~15 | ||||||||||||
| Physical properties | |||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-6748/F-2280 |
| 1、特性：手感柔軟，撕裂性好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：鞋墊、中底 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-6748 | 液狀或石蠟狀 | 700~1200 | 1.080~1.160 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2280 | 液狀或石蠟狀 | 200~600 | 1.090~1.110 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-6748 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2280 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/73~75 | 6~9 | 45~55 | 0.14~0.18 | 45~55 | 5~7 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑的加入量為250±5g/18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | ||||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore C） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | ||||||||||||
| 物性值 | 0.35~0.40 | 50~60 | 14~30 | 250~350 | 20~26 | ||||||||||||
| Physical properties | |||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5335/F-2230 |
| 1、特性：手感好，低硬度，耐寒性好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：耐寒鞋底、連幫鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5335 | 液狀或石蠟狀 | 600~1200 | 1.170~1.190 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2230 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5335 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2230 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/60.5~62.5 | 7~10 | 50~70 | 0.27~0.32 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑的加入量為450±5g/18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -15℃ | |||||||||||
| 物性值 | 0.42~0.52 | 30~40 | 30~50 | 500~700 | 15~25 | 40000次無裂口 | |||||||||||
| Physical properties | |||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-5340/F-2220 |
| 1、特性：手感好，低硬度，耐寒性好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：耐寒鞋底、連幫鞋 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-5340 | 液狀或石蠟狀 | 400~1200 | 1.170~1.190 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2220 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-5340 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2220 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/63.5~65.5 | 7~10 | 50~70 | 0.27~0.32 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑的加入量為360±5g/18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -25℃ | |||||||||||
| 物性值 | 0.42~0.52 | 30~40 | 30~50 | 500~700 | 15~25 | 40000次無裂口 | |||||||||||
| Physical properties | |||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
4
Resin For Labor Insurance Shoe
| HT-2033/F-2580 |
| 1、特性：粘結力高，手感好，耐寒性好 | |||||||||||||||||||
| Characteristic： | |||||||||||||||||||
| 2、用途：雙密度勞保鞋 | |||||||||||||||||||
| Application： | |||||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||||
| HT-2033 | 液狀或石蠟狀 | 1400~2200 | 1.130~1.180 | 18 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| F-2580 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||||
| HT-2033 | 60-70℃預熱6~8h | ||||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||||
| F-2580 | 60-70℃預熱8~12h | ||||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||||
| 技術參數 | 40~45/40~45 | 大底 | 中底 | 4~6 | 30~40 | 大底 | 中底 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||||
| 100/63~65 | 100/104~106 | 0.55~0.7 | 0.22~0.26 | ||||||||||||||||
| ◎催化劑SM-2的加入量為450±5g/18kg The adding content of SM-2 should be 450±5g / 18kg | |||||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||||
| 中底：水H2O 70±5g/18kg，硬化劑800±5g/18kg | |||||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -20℃ | |||||||||||||
| 物性值 | 大底 | 中底 | 大底 | 中底 | 大底 | 中底 | 大底 | 中底 | 中底 | 50000次無裂口 | |||||||||
| Physical properties | 0.9~1.10 | 0.40~0.45 | 66~71 | 45~50 | 50~65 | 35~45 | 550~700 | 400~450 | 20~25 | 50000 times no crack | |||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||||
| HT-8255/F-2561 |
| 1、特性：高粘結力，手感好，耐寒性好 | |||||||||||||||||||
| Characteristic： | |||||||||||||||||||
| 2、用途：雙密度勞保鞋和一次成型休閑鞋 | |||||||||||||||||||
| Application： | |||||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||||
| HT-8255 | 液狀或石蠟狀 | 1500~2200 | 1.120~1.180 | 18 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| F-2561 | 液狀或石蠟狀 | 200~500 | 1.190~1.210 | 20 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||||
| HT-8255 | 60-70℃預熱6~8h | ||||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||||
| F-2561 | 60-70℃預熱8~12h | ||||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||||
| 技術參數 | 40~45/40~45 | 大底 | 中底 | 6~10 | 50~60 | 大底 | 中底 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||||
| 100/74~76 | 100/79~81 | 0.4~0.5 | 0.25~0.35 | ||||||||||||||||
| ◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg | |||||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||||
| 大底: 水H2O 20±5g/18kg | |||||||||||||||||||
| 中底：水H2O 50±5g/18kg | |||||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -10℃ | |||||||||||||
| 物性值 | 大底 | 中底 | 大底 | 中底 | 大底 | 中底 | 大底 | 中底 | 中底 | 50000次無裂口 | |||||||||
| Physical properties | 0.8~1.0 | 0.45~0.65 | 55~75 | 40~60 | >80 | >45 | 350~450 | 300~400 | >20 | 50000 times no crack | |||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||||
| HT-8801G/F-2580G |
| 1、特性：高粘結力，耐寒性好，表皮光亮 | |||||||||||||||||||
| Characteristic： | |||||||||||||||||||
| 2、用途：耐寒勞保鞋和一次性成型休閑鞋 | |||||||||||||||||||
| Application： | |||||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||||
| HT-8801G | 液狀或石蠟狀 | 1000~1800 | 1.116~1.124 | 18 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| F-2580G | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||||
| liquid or waxy solid | |||||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||||
| HT-8801G | F-2580G | ||||||||||||||||||
| 60-70℃預熱6~8h | 60-70℃預熱8~12h | ||||||||||||||||||
| Preheated at 60-70℃ for 6~8h | Preheated at 60-70℃ for 8~12h | ||||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||||
| 技術參數 | 40~45/40~45 | 大底 | 中底 | 6~10 | 35~50 | 大底 | 中底 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||||
| 100/74~76 | 100/81~83 | 0.45~0.55 | 0.23~0.33 | ||||||||||||||||
| ◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg | |||||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||||
| 大底: 水H2O 20±5g/18kg | |||||||||||||||||||
| 中底：水H2O 80±5g/18kg | |||||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -20℃ | |||||||||||||
| 物性值 | 大底 | 中底 | 大底 | 中底 | 大底 | 中底 | 大底 | 中底 | 中底 | 50000次無裂口 | |||||||||
| Physical properties | 0.8~1.0 | 0.45~0.65 | 60~75 | 50~65 | 76~85 | 42~51 | 380~460 | 300~400 | 30~35 | 50000 times no crack | |||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||||
5
Coldtolerant Polyester
| HT-2004/F-2580 |
| 1、特性：中硬度，手感好，耐寒性好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：耐寒鞋底 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-2004 | 液狀或石蠟狀 | 2000~2800 | 1.150~1.170 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2580 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-2004 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2580 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/94~95 | 7~10 | 50~60 | 0.27~0.31 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為220±5g/18kg The adding content of SM-2 should be 220±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -20℃ | |||||||||||
| 物性值 | 0.60~0.65 | 57~62 | 38~45 | 460~530 | 33~38 | 50000次無裂口 | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
6
Transparent Material
| HT-2005/F-2580 |
| 1、特性：中硬度，透明料 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：透明鞋底 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-2005 | 液狀或石蠟狀 | 1000~1600 | 1.150~1.170 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-2580 | 液狀或石蠟狀 | 300~700 | 1.180~1.200 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-2005 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-2580 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/76~78 | 0.9~1.2 | 45~55 | 5~7 | ||||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -10℃ | |||||||||||
| 物性值 | 0.90~1.2 | 57~65 | 80~90 | 550~700 | 55~70 | 50000次無裂口 | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
7
Polyether
| HT-4460/F-4200 |
| 1、特性：耐候性優(yōu)良，低溫柔順性好 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：大底 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-4460 | 液狀或石蠟狀 | 300~700 | 1.000~1.040 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-4200 | 液狀或石蠟狀 | 200~600 | 1.001~1.005 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-4460 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-4200 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/65~67 | 7~10 | 35~50 | 0.30~0.35 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑的加入量為400±5g/18kg The adding content of SM-2 should be 400±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -40℃ | |||||||||||
| 物性值 | 0.60~0.70 | 55~65 | 45~55 | 450~550 | 15~20 | 50000次無裂口 | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||
| HT-4465/F-4230 |
| 1、特性：低溫柔順性好,防滑 | |||||||||||||||||
| Characteristic： | |||||||||||||||||
| 2、用途：大底 | |||||||||||||||||
| Application： | |||||||||||||||||
| 3、原液特性 Typical properties of PU matrix | |||||||||||||||||
| 品名 | 外觀 | 粘度 | 密度 | 包裝 | |||||||||||||
| Name of products | Apperance | Viscosity (cps at 40℃) | Density (g/cm3 at 40℃) | Package(kg) | |||||||||||||
| HT-4465 | 液狀或石蠟狀 | 300~700 | 1.000~1.040 | 18 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| F-4230 | 液狀或石蠟狀 | 200~600 | 1.001~1.005 | 20 | |||||||||||||
| liquid or waxy solid | |||||||||||||||||
| ◎物料理想儲藏溫度：25℃以下 | |||||||||||||||||
| 4、物料預熱 Materials preheat | |||||||||||||||||
| HT-4465 | 60-70℃預熱6~8h | ||||||||||||||||
| Preheated at 60-70℃ for 6~8h | |||||||||||||||||
| F-4230 | 60-70℃預熱8~12h | ||||||||||||||||
| Preheated at 60-70℃ for 8~12h | |||||||||||||||||
| 5、成型條件及反應參數 Typical processing parameters &Reaction parameter | |||||||||||||||||
| 項目 | 物料溫度 | 混合比 | 乳化時間 | 起發(fā)時間 | 泡沫密度 | 模具溫度 | 脫模時間 | ||||||||||
| Items | HT/F Materials temperature(℃) | Mixing ratio (HT+SM)/F(By weight) | Cream time(s) | Rise time(s) | Free foam density (g/cm3) | Mold temperature(℃) | Demolding time( min) | ||||||||||
| 技術參數 | 40~45/40~45 | 100/53~55 | 7~10 | 40~50 | 0.70~0.75 | 45~55 | 3~5 | ||||||||||
| Parameter | |||||||||||||||||
| ◎催化劑的加入量為340±5g/18kg The adding content of SM-2 should be 340±5g / 18kg | |||||||||||||||||
| ◎水和硬化劑根據實際需要添加 The adding content of water and hardener should added to the reality | |||||||||||||||||
| 6、制品性能 Physical properties | |||||||||||||||||
| 項目 | 成型密度 | 硬度 | 拉伸強度 | 伸長率 | 撕裂強度 | 耐折試驗 | |||||||||||
| Items | Molded density (g/cm3) | Hardness （Shore A） | Tensile strength （kg/cm2） | Elongation（%） | Tear strength （kg/cm） | Flexing Endurance Test at -40℃ | |||||||||||
| 物性值 | 0.80~1.10 | 60~65 | 30~35 | 350~400 | 12~16 | 50000次無裂口 | |||||||||||
| Physical properties | 50000 times no crack | ||||||||||||||||
| ◎該物性數據是對6mm厚的試片測試獲得的數據。 | |||||||||||||||||
| These physical data are acquired by testing a sample of 6mm thick. | |||||||||||||||||
| ◎自由泡沫密度會依季節(jié)（溫度、濕度）不同而變化。 | |||||||||||||||||
| Free rise density may vary with temperature &humidity. | |||||||||||||||||
| ◎脫模時間會隨成品厚度的增加而延長。 | |||||||||||||||||
| Demold time may be prolonged with the increase of sold thickness. | |||||||||||||||||
| ◎以上數據及作參考，具體數據以實際操作為準，如需其它物性指標，請與我公司聯(lián)系。 | |||||||||||||||||
| Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us. | |||||||||||||||||